Free-radical functionalized polysaccharides

ABSTRACT

The invention concerns a method for functionalizing polysaccharides using a source or free radicals which forms stable radicals on the polysaccharides structure and wherein the formed radicals reacts with a functionalized unsaturated compound, characterized in that the method comprises two steps: a first step, wherein the free radical on the polysaccharide chain is formed, and a second step, wherein said radical reacts with the unsaturated compound in the absence of the radical source. The invention also relates to the functionalized polysaccharide obtained by this process.

The present invention relates to a new process for introducing functional groups on a large varieties of polysaccharides by using free radical generation.

BACKGROUND OF THE INVENTION

High-energy irradiations have been used in several fields of application.

In the beginning the attention was on degradation processes of polymers. The chains were broken by high-energy irradiation with economical and ecological improvements and an exact process control via the dose was possible.

For instance, in the viscose process, studies on electron beam (EB) irradiation have been made by Fischer and Goldberg since 1980 (Patent DD 1 40747 and M. Lenzinger Ber., 1985, Issue 59, 32-39) and further investigation on the cellulose pulp were carried out by P. Burkart, (Polym. News, 1999, 24/6, 194-197). These studies opened a new route of commercial relevance to pulp activation in the viscose process which also has ecological advantages. With EB treatment on the cellulose pulp, degradation prevails by far on crosslinking and leads to a narrow chain length distribution and an enhanced accessibility of the cellulose, especially after alkali treatment.

More recently, also the crosslinking route was investigated. In WO 01/30407, for example, a polyvinyl alcohol solution in water, containing natural polymers, can be cross-linked using high-energy irradiation to form hydrogels for use in the medical field; the products obtained by this process are described as having qualities of sterility, transparency, cooling effect, biocompatibility, oxygen permeability, absorption, humid environment.

The introduction of functional groups on the polysaccharide chain has been another object of several studies. In particular, studies have shown that it is of great importance the etherification and esterification of cellulose with functional groups to obtain fibers with improved qualities of resistance and applicability.

For instance, an esterification process for preparing polyanhydride cross-linked fibrous cellulosic products is claimed in WO 98/13545 [Amoco Corporation].

However a significant drawback of the esterified and etherified functional derivatives that malces them less attractive from a practical viewpoint is the low stability of ester bonds: in fact they are cleaved under alkaline conditions, as usually happens by repeated laundry, especially with strong detergents.

It is important to obtain functionalization of polysaccharides with functional groups that have stable bonds which, for example do not break in alkaline conditions, so that the polysaccharide does not degrade easily after it is washed with detergents.

European patent application 01830331 discloses a process to functionalize linen by introducing a stable bond at the O of the hydroxyl groups of the polysaccharide structure maintaining the allomorph I state.

However the state of the art does not report any example of functionalizing a polysaccharide by the formation of stable carbon-carbon bonds on the polysaccharide chain.

SUMMARY OF THE INVENTION

The present invention provides a new method of functionalizing polysaccharides using a source of free radicals which form stable radicals on the saccharide chain. These radicals react with an olefin, forming a stable carbon-carbon bond. If the unsaturated compound contains a functional group, this process results in the introduction of functional groups directly bonded to the saccharide chain through carbon-carbon covalent bonds.

In a preferred embodiment, the method is characterized by a first step, wherein the free radical on the polysaccharide chain is formed, and a second step, wherein said radical reacts with the unsaturated compound in the absence of the radical source.

Examples of radical sources usable in the first step are:

-   -   a chemical system, for example H₂O₂/Fe⁺⁺     -   plasma     -   high-energy irradiation, for example electron beam irradiation         (EB).

DETAILED DESCRIPTION OF THE INVENTION

The present invention provides a new method for functionalizing polysaccharides using a source or free radical which forms stable radicals on the polysaccharide structure. These radicals react with a functionalized olefin, forming a stable carbon-carbon bond between the polysaccharide and the precursor of the functional group.

The method is characterized by a first step, wherein the free radical on the polysaccharide chain is formed, and a second step, wherein said radical reacts with the olefin compound in the absence of the radical source.

In a further embodiment the invention provides new polysaccharides obtainable by the above process and characterized by the presence of functional groups bonded to the polysaccharide chain through carbon-carbon bonds.

In another embodiment the invention provides a process for the preparation of functionalised polysaccharides or polymer fibers which process comprises:

-   -   1. forming stable radicals on the polysaccharide from a free         radical source; and     -   2. reacting in the absence of the free radical source an olefin         containing a functional group with the stable radicals on the         polysaccharide.

A large variety of polysaccharides can be functionalized using the present process. From the industrial point of view the preferred polysaccharides comprise starch or cellulose materials such as cotton, flax, viscose, paper or softwood pulp, or combinations thereof. They can also be used together with one or more natural or synthetic fibers such as, for example, silk, polyamide, polyester, polyacrylate and polyolefin.

By the term olefin we mean any suitable unsaturated (alkene or alkyne) compound capable of reacting with radicals to form a covalent bond.

The choice of the olefin compound depends on the functionalization to be introduced. The amount of olefin compound introduced in the second step of the process, depends directly on the desired lengths of the thelomeric chain that will be attached to the polysaccharide chain.

Preferably, the polysaccharide is cellulose or a derivative thereof, more preferably a naturally sourced cellulose. In another embodiment of the invention, the polysaccharide is in the form of a fiber.

The present invention relates, for example, to the functionalization of flax with functionalized olefins such as glycidylmethacrylate (GMA) and allylglycidylether (AGE). Every kind of source which is able to generate free radicals, may be used. Preferred free radical sources are:

-   -   a chemical system, for example Fenton's reagent (H₂O₂/Fe⁺⁺)     -   plasma     -   high-energy irradiation, for example electron beam irradiation         (EB).

Hydrogen peroxide is reduced by Fe²⁺ salts to hydroxyl radical and hydroxyl anion. As hydroxyl radical easily abstracts hydrogen atoms, Fenton's reagent can be considered a useful tool to generate carbon centred radical.

Plasma is a partially ionized gas that consists of ions, electrons, and neutral particles. It is well-known that the plasma treatment may be very efficient and useful to change permanently the surface properties of fibres in yarn or fabrics. It is therefore a suitable method to generate free-radicals on the surface of yarns and fabrics.

Electron beam irradiation is a radiochemical method convenient and effective, especially because of its moderate initiation reaction conditions, i.e. atmospheric pressure and room temperature. As the electron beam penetrates the matter, electron beam treatment can induce deep modifications of fibers.

In the case of Fenton's reagent, it is preferred to use a ratio mol H₂O₂/eq anh. glucose comprised between 100:1 and 1:1, more preferably between 50:1 and 5:1. The amount of Fe²⁺ can vary considerably and the molar ratio H₂O₂/Fe²⁺ varies generally between 1 and 10⁵, preferably between 10 and 10⁴.

Cold plasma irradiation can be performed in a broad range of conditions. Preferably the power is fixed in the range 50-500 W and the treatment is performed for a time comprised between a 10 seconds and 15 minutes, more preferably between 1 minute and 10 minutes. EB activation can be performed in a broad range of radiation energy. Preferably the energy can range from 100 keV to 5 MeV. However, since it is well known that it also induces depolymerization of the polysaccharide, it is convenient to use a radiation dose comprised between 10 and 400 kGy, preferably between 20 and 200 kGy, most preferably between 40 and 150 kGy. As indicated in Tables 10-12, the radicals generated on the polysaccharide are stable for a long period of time, with a half life time of about 1 day. As a consequence, it is possible to irradiate a polysaccharide and transport it to another plant where the second step is performed. Thus, the radiation dose will depend not only on the amount of functional groups to be introduced, but also on the time between the first and second step.

The type of olefin used is not particularly limited. In fact, although the stable radicals generated on the polysaccharide are generally definable as nucleophilic radicals, it is possible to add them either to electron-poor olefins such as GMA or to non activated olefins such as AGE.

Basically, the choice of the olefin will depend on several factors amongst which the most important will be the type of functional group that will be finally present on the polysaccharide. In fact, the glycidyl group of GMA and AGE can be further reacted according to well known methods of synthetic organic chemistry to give rise to a large variety of functional groups pending from the saccharide backbone.

The amount of functional groups introduced in the polysaccharide can be measured by the ratio mol olefin/eq anhydrous glucose. This ratio can vary in a broad range and is preferably comprised between 10⁻³ and 2, more preferably between 10⁻² and 1.

Experimental Part

Characterization of the Products

EPR

Signals Observed for Irradiated Powder Samples of Polysaccharides

Powdered flax was put inside a quartz tube of 4 mm internal diameter to reach about 15 mm height. The tube was weighted and the amount of flax (w_(x)) calculated (about 25 mg). All the measurements were taken using the following parameters:

-   -   Central Magnetic Field: 331.0 mT     -   Scan Width: 100 G     -   Number of points: 2048     -   Receiver Gain: 1e4     -   Modulation Amplitude: 0.1 mT     -   Attenuation: 15 dB.

The value of the signal intensity (I_(x)) was determined as following: I _(x)=(∫∫s _(x)×200/w _(x))×∫∫r ₁ /∫∫r _(x) Where:

-   -   ∫∫s_(x) is the spectrum double integrations of the of the Whole         scan Range     -   ∫∫r_(x) is the spectrum double integrations of the signal of a         Standard crystal synthetic Ruby     -   ∫∫r₁ is the value for the first sample considered as Reference         NMR

Solid state ¹³C CPMAS spectra were recorded with a Bruker ASX-300 spectrometer equipped with a 7 mm WB CPMAS probe head. Samples were finely powdered, packed into 7 mm zirconia rotor and sealed with Kel-F caps. The spinning speed of the sample was 4 Khz.

The π/2 pulse was 3.7 μsec, the contact time for the cross-polarization experiment was 1.2 ms, and the relaxation delay was 6 s. Spectra were obtained with 1024 data points in the time domain, 512 scans were performed for each experiment.

FR-IR

The samples were ground with infrared grade KBr in an agate mortar. 500 mg of IBr were mixed with the sample (2% w/w). The translucent discs, obtained by pressing the ground material with aid of a press, were analyzed in transmission with an IFS 25 Bruker spectrometer. 64 scans were sufficient for good resolution.

The ester characteristic signal was evaluated for every sample to define the real functionalization. The area of the ester band was normalized referring to another characteristic cellulose band: area_(N(ester))=[area_(ester)(manual band integration)/area_(cellulose)(range 780−465 cm⁻¹integration)]×100

EXAMPLE 1 Activation by Fenton's Reagent and Functionalization with GMA

Comparative Run 1.1

In a three-neck round bottom flask, flax (Emerald Sliver, 0.807 g) powdered with a blade-mill, was dipped into a 50 ml of H₂O. 5.27 ml H₂O₂ 12 M were added to reach a concentration of 1.2 M. The mixture was warmed up to 80° C.

100 μl of a saturated FeSO₄ heptahydrate solution (5.62 10⁻² mmol, 9.0 10⁻⁴ mol Fe⁺²/mol H₂O₂) were added dropwise. The reaction lasted 30 min.

The solid material was removed, washed with abundant cool water and filtered.

Run 1.2

In a three-neck round bottom flask, Emerald Sliver (0.807 g) powdered with a blade-mill, was dipped into a 50 ml of H₂O. 5.27 ml H₂O₂ 12 M were added to reach a concentration of 1.2 M. The mixture was warmed up to 80° C. 100 μl of a saturated FeSO₄ solution (5.62 10⁻² mmol, 9.0 10⁻⁴ eq Fe⁺²/eq H₂O₂) was added dropwise. The reaction lasted 30 min.

The solid material was removed, washed with abundant cool water and filtered.

The obtained material was dipped into a methanol-water 1:1 solution (100 ml) containing glycidylmethacrilate (20% vol) and left reacting for one hour at 80° C. under argon flux. The reaction mixture was cooled, the solid was removed and washed with water-methanol at 80° C., then with water-methanol at room temperature, and finally three times with acetone at room temperature.

The material was dried in air until a constant weight was reached (1.497 g).

Run 1.3

In a three-neck round bottom flask, a little hank of Emerald Sliver (2.275 g) was dipped into 146 ml of water. H₂O₂ 40 vol % (14.6 ml=172 mmole, 12.44 (eq H₂O₂)/(eq Anhydrous glucose)) was added to reach a final concentration of 4% vol.

The mixture was warmed up to 80° C.

280 μl of a saturated FeSO₄ heptahydrate solution (15.7 10⁻² mmol, 9.0 10⁻⁴ mol Fe⁺²/mol H₂O₂) were slowly added.

The reaction lasted 120 min.

The solid material was removed, washed with abundant cold water and filtered.

A part of the obtained material (1.7751 g) was dipped into a methanol-water 1:1 solution (180 ml) containing glycidylmethacrilate (20% vol) and left reacting for one hour at 80° C. under argon flux.

The reaction mixture was cooled, the solid was removed and washed with water-methanol at 80° C., then with water-methanol at room temperature, and finally three times with acetone at room temperature.

The material was dried in air until a constant weight was reached (2.8924 g).

FIGS. 1, 2 and 3 show respectively the IR spectra of the Sliver before treatment, after treatment, and after reaction with GMA. It is possible to see that the treatment with Fenton's reagent does not produce any change in the IR spectrum, while reaction with GMA introduces a band at 1725 cm⁻¹, typical of the presence of an ester group. TABLE 1 Reaction Fe²⁺/H₂O₂ GMA GMA/Aglu area_(N (ester)) Run Time mole/mole [M] mol/mol FT-IR Comp. 1.1  30′ 9 × 10⁻⁴ — — 7.2 10⁻³ 1.2  30′ 9 × 10⁻⁴ 1.5 30 0.98 1.3 120′ 9 × 10⁻⁴ 1.5 20 0.43 1.4  30′ 9 × 10⁻³ 1.4 10 0.52

EXAMPLE 2 Activation by Cold Plasma and Functionalization with GMA

Plasma Activation

A variable amount (5-12 g) of the starting material was treated with Cold Plasma (Power 200 W) at the pressure of 0.2 mbar under Argon.

The experiments were carried out under the following conditions.

The sample was put inside the chamber of the instrument on the appropriate support and the valve which connects the chamber to the rotative pump was open so that the Argon was stripped out of the sample and the pressure was decreased to 0.2 mbar. When the conditions were stabilized, the rf generator was put on (Power fixed on 200 W) to generate the discharge (Plasma Chamber). The Plasma treatment was carried out for 180 sec. Then the generator was put off and both the pomp valve and the Argon cylinder pin-valve were closed. Another valve was open to introduce air inside the chamber until atmospheric pressure was reached.

Comparative Run 2.1

A hank of Emerald Sliver (9.29 g), was treated with PLASMA. In Table 2 the value of area_(N (ester)) is reported by comparison.

Run 2.2

In a tree-neck round bottom flask, a 300 ml solution of methanol-water 1:1 vol, containing AGE (20% vol), under nitrogen flux, was stirred for 30 min at 80° C.

A hank of Emerald Sliver (9.29 g), previously treated with PLASMA was added in the reaction solution; the mixture was left to react for five hours under these conditions and then cooled down. The solid material was recovered and treated for 30 min at 80° C. with 300 ml of methanol-water 1:1, for 30 min at room temperature with 200 ml methanol-water 1:1 and then washed three times with 200 ml of acetone.

The purified material was dried in air until a constant weight was reached (9.90 g).

Run 2.3

In a tree-neck round bottom flask, a 200 ml solution of methanol-water 1:1 vol, containing GMA (20% vol), under nitrogen flux, was stirred for 30 min at 80° C.

A hank of Emerald Sliver (2.87 g), previously treated with Plasma was added in the reaction solution; the mixture was left to react for one hour under these conditions and then cooled down. The solid material was recovered and treated for 30 min at 80° C. with 150 ml of methanol-water 1:1, for 30 min at room temperature with 150 ml methanol-water 1:1 and then washed three times with 100 ml of acetone.

The purified material was dried in air until a constant weight was reached: (2.99 g).

FIG. 1 shows the IR spectrum of Emerald Sliver without treatments. In FIG. 4 the IR spectrum of the functionalized Sliver is shown. It is possible to see the signal at 1726 cm⁻¹.

Comparative Run 2.4

A cotton fabric piece (cotton 100%, 5.63 g) was treated with Plasma. In Table 2 the value of area_(N(ester)) is reported by comparison.

Run 2.5

In a tree-neck round bottom flask, a 200 ml solution of methanol-water 1:1 vol, containing GMA (20% vol), under nitrogen flux, was stirred for 30 min at 80° C.

A cotton fabric piece (cotton 100%, 5.63 g), previously treated with Plasma was added in the reaction solution. The mixture was left to react for one hour under these conditions and then cooled down. The solid material was recovered and treated for 30 min at 80° C. with 150 ml of methanol-water 1:1, for 30 min at room temperature with 150 ml methanol-water 1:1 and then washed three times with 100 ml of acetone.

The purified material was dried in air until a constant weight was reached (5.79 g).

Comparative Run 2.6

A mixed cotton fabric piece (cotton 52%, viscose 43%, elastan 5%, 10.52 g), was treated with Plasma. In table 2 the value of area_(N(ester)) is reported by comparison.

Run 2.7

In a tree-neck round bottom flask, a 300 ml solution of methanol-water 1:1 vol, containing GMA (20% vol), under Nitrogen, was stirred for 30 min at 80° C.

A mixed cotton fabric piece (cotton 52%, viscose 43%, elastan 5%, 10.52 g), previously treated with Plasma was added in the reaction solution. The mixture was left to react for to one hour under these conditions and then cooled down. The solid material was recovered and treated for 30 min at 80° C. with 250 ml of methanol-water 1:1, for 30 min at room temperature with 250 ml methanol-water 1:1 and then washed three times with 200 ml of acetone.

The purified material was dried in air until a constant weight was reached (10.61 g). TABLE 2 Time Reaction Olefin before Olefin/Aglu Product area_(N(ester)) Run Material [M] reaction mol/mol Olefin/Aglu FT-IR Comp. 2.1² Emerald — — — — 6.87 10⁻³ Sliver 2.2 Emerald AGE 9    9.2 × 10⁻² — Sliver 1.60 2.3 Emerald GMA 1 day  16    5.0 × 10⁻² 3.73 × 10⁻² Sliver 1.50 Comp. 2.4² Cotton — — — —  5.8 × 10⁻³ 100% 2.5 Cotton GMA 1 day  8.5  3.3 × 10⁻² 3.57 × 10⁻² 100% 1.50 Comp. 2.6² Cotton 52% — — — — 1.64 × 10⁻³ Viscose 43% Elastan 5% 2.7 Cotton 52% GMA 6 days 8.5 0.93 × 10⁻² 0.67 × 10⁻² Viscose 43% 1.50 Elastan 5% ¹Determinated by weighing. ²Only plasma activation.

EXAMPLE 3 Activation of Emerald Sliver with EB and Functionalization with GMA and AGE

Activation by Electron-Beam (EB)

A variable amount (0.5-20 g) of the material to irradiate was treated with Electron Beam (radiation dose 20-400 kGy). Irradiations were carried out by putting the sample on the rotating cylinder. The samples were put inside mylar (PET) pocket.

The radiation dosing was made before irradiating using a Crosslinking-DOSE READER DR 020. The cylinder rotated at the frequency of 1 turn/10 s, and the obtained dose/turn values were about 8 kGy (with an Electron Beam of 300 keV Energy and 2 mA Current).

Run 3.1

In a tree-neck round bottom flask, a 200 ml solution methanol-water 1:1 vol, containing GMA (5% vol), under Nitrogen flux, was stirred for 30 min at 80° C.

A hank of Emerald Sliver (4.23 g), previously treated with Electron Beam (20 kGy) was added to the solution and the reaction kept thermostated and under stirring for an hour. The mixture was then cooled down. The solid material was recovered and treated for 30 min at 80° C. with 150 ml of methanol-water 1:1, for 30 min at room temperature with 100 ml methanol-water 1:1 and then washed three times with 150 ml of acetone.

The purified material was dried in air until a constant weight was reached (4.3856 g).

Runs 3.2-3.13

The runs were performed according to the general procedure described for run 3.1, according to the conditions specified in table 3.

FIG. 5 shows the NMR ¹³C spectrum of run 3.7 wherein it is possible to see that flax remains in the allomorph state I. TABLE 3 Time Reaction Product EB area_(N(ester)) Before Olefin Olef./Aglu Olefin/Aglu¹ Run Activation FT-IR reaction [M] mol/mol mol/mol area_(N(ester)) 3.1  20 kGy - N₂ 1.05 × 10⁻² — GMA 3.0   4 10⁻² 6.3 10⁻² 0.35 3.2  40 kGy - N₂ 1.79 × 10⁻² — GMA 3.0 0.40 0.46 0.35 3.3  60 kGy - N₂  1.3 × 10⁻² — GMA 3.0 0.47 0.47 0.35 3.4  80 kGy - N₂ 1.55 10⁻² — GMA 3.0 0.80 0.79 0.35 3.5  80 kGy - air  1.2 × 10⁻² — GMA 3.0 0.66 0.62 0.35 3.6 100 kGy - N₂  9.4 × 10⁻³ — GMA 6.0 1.1 0.9 1.40 3.7 100 kGy - N₂ nd 19 days GMA 3.0 0.3 0.37 0.35 3.8 150 kGy - N₂  1.3 × 10⁻² — GMA 3.0 1.1 0.7 0.35 3.9 200 kGy - N₂ nd 11 days GMA 3.0 1.2 0.95 0.35 3.10 200 kGy - N₂ nd 18 days GMA 3.0 0.58 0.51 0.35 3.11 400 kGy - N₂ nd  1 day  GMA 20.0 12.5 12.0 1.70 3.12 400 kGy - N₂ nd  7 days GMA 10.0 2.9 2.3 0.35 3.13 100 kGy - N₂ nd — AGE 7.0 3.71 10⁻² Nd 2.00 ¹By weighing nd = not determined

COMPARATIVE EXAMPLE 4 Activation with EB of Flax Impregnated with GMA

Flax hank was impregnated with solutions of GMA under stirring for 2 hours.

The hank was removed, and dried several hours in air until a constant weight was reached.

The material was treated under nitrogen with Electron Beam, dose 50-100 kGy. The irradiated material was exhaustively washed with water-methanol at 80° C., then with water-methanol at room temperature, and finally with acetone (three times) at room temperature.

The material was dried in air until a constant weight was reached.

Table 4 reports the results obtained by this procedure and proves that the use of a single-step procedure does not lead to introduction of functional groups on the polysaccharide. TABLE 4 Wt increase hank flax Product GMA in after EB GMA/Agluc¹ area_(N(ester)) Run acetone % impregn. (kGy) mol/mol FT-IR 4.1 10 18%  50 nd 0.86 × 10⁻² 4.2 10 20% 100 1.17 × 10⁻² 1.16 × 10⁻² 4.3 20 56%  50  2.2 × 10⁻² 2.52 × 10⁻² 4.4 20 60% 100 3.26 × 10⁻²  3.0 × 10⁻² ¹By weighing after reaction and repeated washings nd = not determined

EXAMPLE 5 Activation with EB and Functionalization of Quartz Sliver with GMA

Run 5.1

In a tree-neck round bottom flask, a 300 ml solution of methanol-water 1:1 vol, containing GMA (5% vol), under nitrogen flux, was stirred for 30 min at 80° C.

A hank of flax (Quartz Sliver, 5.15 g), previously treated with Electron Beam (100 kGy) was added in the reaction solution. The mixture was left to react for one hour under these conditions and then cooled down. The solid material was recovered and treated for 30 min at 80° C. with 150 ml of methanol-water 1:1, for 30 min at room temperature with 100 ml methanol-water 1:1 and then washed three times with 150 ml of acetone.

The purified material was dried in air until a constant weight was reached (5.99 g).

Run 5.2

In a tree-neck round bottom flask, a 150 ml solution methanol-water 1:1 vol, containing GMA (20% vol), under Nitrogen flux, were stirred for 30 min at 80° C.

A hank of Quartz Sliver (5.5 g), previously treated with Electron Beam (100 kGy) was added in the reaction solution. The mixture was left to react for one hour under these conditions and then cooled down. The solid material was recovered and treated for 30 min at 80° C. with 150 ml of methanol-water 1:1, for 30 min at room temperature with 100 ml methanol-water 1:1 and then washed three times with 150 ml of acetone.

The purified material was dried in air until a constant weight was reached (13.8 g).

Run 5.3

In a tree-neck round bottom flask, a 200 ml solution methanol-water 1:1 vol, containing AGE (5% vol), under Argon flux, was stirred for 30 min at 80° C.

A hank of Quartz Sliver (5.52 g), previously treated with Electron Beam (100 kGy), was added in the reaction solution. The mixture was left to react for one hour under these conditions and then cooled down. The solid material was recovered and treated for 30 min at 80° C. with 150 ml of methanol-water 1:1, for 30 min at room temperature with 100 ml methanol-water 1:1 and then washed three times with 100 ml of acetone.

The purified material was dried in air until a constant weight was reached (5.55 g). TABLE 5 Time Reaction Product EB Olefin before Olefin/Aglu Olefin/Aglu area_(N(ester)) ² Run (kGy) [M] funct. mol/mol mol/mol¹ FT-IR 5.1 100 GMA — 3.0  0.18 0.17 0.35 5.2 100 GMA — 6.0 1.7 1.58 1.20 5.3 100 AGE — 9.0 1.47 × 10⁻² — 2.50 5.4 400 GMA 12 3.0 1.5 1.42 0.35 days ¹By weighing ²area_(N(ester))not-treated sliver: 4.29 × 10⁻³

EXAMPLE 6 Activation of Emerald Yarn with EB and Functionalization with GMA

In a tree-neck round bottom flask, a 50 ml solution methanol-water 1:1 vol, containing GMA, under nitrogen flux, was stirred for 30 min at 80° C.

A hank of flax fiber (Emerald Yarn) previously treated with Electron Beam (400 kGy) was added in the reaction solution. The mixture was left to react for one hour under these conditions and then cooled down. The solid material was recovered and treated for 30 min at 80° C. with 150 ml of methanol-water 1:1, for 30 min at room temperature with 100 ml methanol-water 1:1 and then washed three times with 150 ml of acetone.

The purified material was dried in air until a constant weight was reached.

The different conditions used in runs 6.1 and 6.2 are reported in Table 6 TABLE 6 Time Reaction before GMA GMA/Aglu GMA/Agluc¹ area_(N(ester)) Run funct. [M] mol/mol mol/mol FT-IR 6.1 5 days 1.40 23.0 6.1 5.29 6.2 8 days 0.35  7.0 3.8 1.96 ¹By weighing

EXAMPLE 7 Activation of Cotton with EB and Functionalization with GMA

A serie of runs using various cotton materials was performed according to the procedure of example 6. The runs were performed at 70° C. for an hour with a concentration of GMA 0.8 M (GMA/Agluc=5.0). Other specific conditions are reported in Table 7. TABLE 7 EB Product activation GMA/Agluc¹ area_(N(ester)) Run Material (kGy) mol/mol FT-IR 7.1 Mercerized 100 - N₂ 2.2 10⁻² 4.07 × 10⁻³ Cotton² 7.2 Mercerized 200 - N₂ 1.39 1.56 Cotton² 7.3 Cotton³ 100 - N₂ 2.7 1.72 7.4 CottonWool⁴ 150 - N₂ 0.93 0.65 7.5 CottonWool⁴ 150 - Air 0.57 3.36 × 10⁻² ¹By weighing ²area_(N(ester)) not-treated = 9.2 10⁻⁴ ³area_(N(ester)) not-treated = 3.55 10⁻⁴ ⁴area_(N(ester)) not-treated = 4.6 10⁻⁴.

EXAMPLE 8 Activation of Cotton-Viscose-Elastan with EB and Functionalization with GMA

Two runs were performed on a cotton52% viscose43% elastan5% fiber.

The results and the conditions applied are reported in Table 8. TABLE 8 Time Reaction before GMA GMA/Agluc¹ area_(N(ester)) Run EB (kGy) funct. [M] mol/mol FT-IR¹ 8.1 200 2 days 0.8 13 3.42 × 10⁻² 8.2 300 — 1.7 25 0.37 ¹area_(N(ester)) not-treated = 5.07 × 10⁻³

EXAMPLE 9 Activation of Various Polysaccharides with EB and Functionalization with GMA

The procedure of example 6 was applied to samples of various polysaccharides. The results and the conditions applied are reported in Table 9 TABLE 9 EB Time Reaction activation before GMA/Agluc area_(N(ester)) Run Material (kGy) funct. GMA [M] mol/mol FT-IR 9.1 Microcrystalline 100 - N₂ — 0.8 3 0.10 Cellulose¹ 9.2 Microcrystalline 200 - N₂ — 0.8 3 0.47 Cellulose¹ 9.3 Microcrystalline 200 - Air — 0.8 3 0.28 Cellulose¹ 9.4 Single-filament 200 - N₂ 1 day 0.8 10   5.7 × 10⁻² Viscose² 9.5 Maize Starch³ 200 - N₂ 1 day 0.8 3 3.11 × 10⁻² 9.6 Maize Starch³ 300 - N₂ — 2.0 3  7.4 × 10⁻² ¹area_(N(ester)) not-treated = 9.2 10⁻⁴ ²area_(N(ester)) not-treated = 1.77 10⁻³; area_(N(ester)) EB activated = 2.3 10⁻² ³area_(N(ester)) not-treated and treated with EB = 0.0

TABLE 10 EPR signals change in time for flax irradiated samples Days Material 0 1 4 5 14 21 28 Quartz Sliver 400 kGy 7.35 E9 3.69 E9 2.24 E9 2.43 E9 1.70 E9 1.38 E9 1.22 E9 Quartz Sliver 200 kGy 5.83 E9 3.24 E9 1.93 E9 2.00 E9 1.35 E9 1.33 E9 1.06 E9 Quartz Yarn 400 kGy 4.25 E9  2.3 E9 2.41 E9 1.14 E9 0.95 E9 0.86 E9 Quartz Yarn 200 kGy 3.82 E9 1.25 E9 1.54 E9 1.47 E9 1.215 E9  1.01 E9 Emerald Sliver 400 kGy 5.29 E9  2.5 E9 2.47 E9 1.19 E9 0.98 E9 0.91 E9 Emerald Sliver 200 kGy 3.94 E9 1.79 E9 1.76 E9 1.65 E9 1.27 E9 1.03 E9 Emerald Yarn 400 kGy 8.81 E9 4.13 E9 2.57 E9 2.73 E9 1.56 E9 1.18 E9 0.99 E9 Emerald Yarn 200 kGy 4.35 E9 1.74 E9 1.88 E9 1.78 E9 1.19 E9 1.10 E9

TABLE 11 EPR signals change in time for various irradiated (200 KGy) samples Days Material 0 1 2 3 7 14 22 32 51 Textil 1 3.47 E9 2.27 E9 1.95 E9 1.89 E9 1.42 E9 1.27 E9 1.13 E9 1.12 E9 1.08 E9 Textil 2 1.92 E9 1.66 E9 1.37 E9 1.41 E9 1.13 E9 1.00 E9 0.87 E9 0.79 E9 0.89 E9 Textil 3 3.80 E9 2.83 E9 2.59 E9 2.52 E9 2.00 E9 1.77 E9 1.55 E9 1.40 E9 1.53 E9 Viscose 4.14 E9 1.20 E9 0.81 E9 0.79 E9 0.62 E9 0.57 E9 0.50 E9 0.49 E9 0.52 E9 Starch 0.48 E9 0.085 E9  0.080 E9  0.050 E9  0.042 E9  0.031 E9  0.027 E9  0.024 E9  0.020 E9  Textil 1 = Cotton 52%, Viscose 43%, Elastan 5% Textil 2 = Cotton 70%, Polyester 30% Textil 3 = Cotton 85%, Silk 15%

TABLE 12 EPR signals change in time for various irradiated (300 KGy) samples Days Materials 0 1 2 3 6 10 17 35 Cotton 5.97 E9 3.85 E9  3.15 E9  3.05 E9  2.58 E9  2.19 E9  2.13 E9  1.89 E9 Textil 1 4.80 E9 2.79 E9  2.22 E9  2.16 E9  1.80 E9  1.71 E9  1.57 E9  1.40 E9 Starch 0.66 E9 0.11 E9 0.061 E9 0.053 E9 0.038 E9 0.022 E9 0.020 E9 0.023 E9 Textil 1 = Cotton 52%, Viscose 43%, Elastan 5% 

1. Method for functionalizing polysaccharides using a source of free radicals, which forms stable radicals on a polysaccharide structure, wherein at least one of the formed radicals reacts with a functionalized olefin, comprising: a first step, wherein a free radical on a polysaccharide chain is formed, and a second step, wherein said radical reacts with an olefin in the absence of a radical source; and the polysaccharide is in the form of a fiber.
 2. Method according to claim 1, wherein a source of free radicals is a chemical source or a physical source.
 3. Method according to claim 2, wherein the physical source is selected from cold plasma and electron beam radiation, and the chemical source is Fenton's reagent.
 4. Method according to claim 1, wherein the polysaccharide is selected from the group consisting of flax, cellulose, viscose and cotton.
 5. Method according to claim 4, wherein the polysaccharide is used together with one or more natural or synthetic fibers.
 6. Method according to claim 5, wherein the natural or synthetic fibers are selected from silk, polyamide, polyester, polyacrylate and polyolefin.
 7. Method according to claim 1, wherein, in the first step, the free radical is generated by electron beam having a radiation dose between 10 and 400 kGy.
 8. Method according to claim 7, wherein the radiation dose is between 20 and 200 kGy.
 9. (canceled)
 10. Method according to claim 1, wherein the stable radicals have a half-life of about 1 day.
 11. Polysaccharides obtainable by the method of claim
 1. 12. Polysaccharides according to claim 11, wherein a ratio mol olefin/eq anhydrous glucose is between 10⁻³ and
 2. 13. Process for the preparation of functionalized polysaccharides or polymer fibers comprising: a) forming stable radicals on a polysaccharide from a free radical source; and b) reacting, in the absence of the free radical source, an olefin containing a functional group with the stable radicals on the polysaccharide.
 14. Polysaccharides according to claim 12, wherein the ratio is between 10⁻² and
 1. 